主要材料是由氧化钇和氧化锆组成的部分稳定二氧化锆。
| 功能特点 |
|---|
- 珠子的微结构分布均匀
- 高强度，高韧性→带来高耐磨性（对物料污染小），生产稳定。
- 高密度→高分散率
| 物理性能，组成 | ||
|---|---|---|
| 组成[wt%] | ZrO2 | 94.75±0.60 |
| Y2 O3 | 4.90±0.50 | |
| Al2 O3 | 0.30±0.10 | |
| Fe2 O3 | ≦0.01 | |
| SiO2 | ≦0.01 | |
| TiO2 | ≦0.01 | |
| MgO | ≦0.01 | |
| Na2 O3 | ≦0.01 | |
| 硬度（Hv） | 1250 | |
| 韧性[MPam0.5] | 6 | |
| 密度[g/cm 3] | 6.0 | |
| 尺寸和规格 | |||
|---|---|---|---|
| Beads size[mm] | 粒径允许范围（mm） | 平均压坏荷重（kgf） | |
| + | - | ||
| 0.1 | 0.03 | 0.02 | more than 1 |
| 0.2 | 0.05 | 0.05 | more than 3 |
| 0.3 | 0.1 | 0.05 | more than 6 |
| 0.4 | 0.1 | 0.1 | more than 10 |
| 0.5 | 0.1 | 0.1 | more than 20 |
| 0.65 | 0.15 | 0.15 | more than 30 |
| 0.8 | 0.1 | 0.1 | more than 50 |
| 1 | 0.2 | 0.2 | more than 80 |
| 1.25 | 0.2 | 0.2 | more than 120 |
| 1.5 | 0.2 | 0.2 | more than 160 |
| 1.75 | 0.2 | 0.2 | more than 200 |
| 2 | 0.2 | 0.2 | more than 240 |
| 2.35 | 0.25 | 0.25 | more than 270 |
| 2.5 | 0.25 | 0.25 | more than 300 |
| 3 | 0.3 | 0.3 | more than 500 |
| 4 | 0.4 | 0.4 | more than 540 |
| 5 | 0.5 | 0.5 | more than 600 |